  • Pre-Baked Carbon Anodes for Electrolytic Aluminum Production
Pre-Baked Carbon Anodes for Electrolytic Aluminum Production

Pre-Baked Carbon Anodes for Electrolytic Aluminum Production

Baked Carbon Anodes
Shanchun® Carbon – China’s leading Carbon Anode supplier. whatsapp +8615731101397 !

Pre-baked anode for aluminium electrolysis

Pre-baked carbon anodes are in a leading position of the aluminum industry. The main function of the pre-baked anode is to introduce electricity current into the electrolytic cell during the aluminum electrolysis process and participate in the electrochemical reaction.

Shanchun® Carbon mainly supply pre-baked anodes for electrolytic aluminum. The products have various sizes, among them, 1450mm and 1500mm pre-baked anode blocks are widely used in major aluminum smelters. One of our company's products, slotted anodes, is a new energy-saving and power-saving carbon product, which is popular with users at home and abroad. Its production process and product performance are also advanced in the world.

Prebaked Carbon Anode is made from raw materials such as petroleum coke and coal tar pitch, and then processed by mixing, extruding, high-temperature baking and other processes. It is used as a conductive anode in the electrolytic cell of primary aluminum smelter aluminum. Baked anode has the characteristics of low ash content, low sulfur content, good plasticity and high strength.

Physical and Chemical Specifications

Mainly 1450*660*540, and can also be processed according to customer drawings.

 

Item

 

Unit

 

Guarantee Value

Typical Value

Apparent Density

G/cm3

1.56(Min)

1.56 to 1.60

Electrical Resistivity

Microohm-mu

56(Max)

52.0-56.0

Real Density

G/cm3

2.06(Min)

2.06-2.10

Compress strength

Mpa

38(Min)

38-45

CO2 reactivity

Residue

%

91(Min)

91-95

Ash

%

2.5max

1.0-2.5

Air Reactivity

Residue

%

92(Min)

93-97.5

Ash

%

2)

0.1-2.0

Thermal Conductivity

W/mk

3.0(Min)

3.0-4.5

Flexural Strength

Mpa

9.0(Min)

9.0-13.0

Permeability

NPm

2.3(Max)

0.5-2.3

Thermal Exposure

k-1

4.0*10-6Max

3.0-4.0

Ash

%

0.3(max)

0.5-2.3

Fe

ppm

374(max)

580-374

Si

ppm

275(max)

540-275

S

%

1.2(max)

1.0-1.2

Ni

ppm

250(max)

250-182

V

ppm

150(max)

69-150

Na

ppm

100(max)

42-100

 

Advantages
1. High antioxidant
2. High thermal shock resistance
    Coefficient of thermal expansion 4×10  
    Thermal conductivity 3 W/mk
3. High current density
    The current density 0.8A/cm2
4. Low electrical resistance
    Electrical Resistivity : 55-56μΩm